| About |
|---|
| Ultramid B3S Q661 is a general purpose, PA6 resin for injection molding. Applications Ultramid B3S Q661 is suitable for wide range of applications due to its rapid cycling and excellent physical properties.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Quick molding cycle,Grease resistance,V-2 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 145 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3200 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 79.0 | MPa | ASTM D638 |
| Yield, 23 ℃ | 85.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.2 | % | ASTM D638 |
| Yield, 23 ℃ | 3.8 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2740 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180 |
| 23℃ | 53 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 76.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 65.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 180 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| 0.75 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 75.0 | ℃ | UL 746 |
| 3.0 mm | 75.0 | ℃ | UL 746 |
| 1.5 mm | 110 | ℃ | UL 746 |
| 3.0 mm | 115 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 240 to 285 | °C | |
| Mold temperature | 65 to 80 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |