| About |
|---|
| An halogen-free flame retardant injection molding grade with outstanding free-flow properties, with good electrical properties and low smoke density; resistant to glow wire test GWFI to 960°C.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low smoke,Halogen free,Flame Characteristics,Grease resistance,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 80.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6000 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 95.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 5700 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 150 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 3.4 | kJ/m² | ISO 179 |
| 23℃ | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 35 | kJ/m² | ISO 179 |
| 23℃ | 40 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 170 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| 0.71 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.71 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 125 | ℃ | UL 746 |
| 3.0 mm | 125 | ℃ | UL 746 |
| 0.71 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 1 MHz | 3.80 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.015 | IEC 60250 | |
| Compared to the leakage tracing index | 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.71 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 250 to 275 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20000 h |
| 3. 5000 h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |