| About |
|---|
| Ultramid B3WG13 BK00102 is a 63% glass reinforced, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldability and outstanding surface appearance. Potential applications are mirror brackets, fuel lids, gas-assisted steering wheel inserts, ski bindings and bike rack clamps.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good Electrical Properties,Renewable resources,Food contact compliance,Block Copolymer,Inoxidizability,Ozone resistance,Good coloring,HB |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.74 | g/cm³ | ASTM D792 |
| Density | 1.74 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 22000 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 235 | MPa | ISO 527-2 |
| Fracture, 23 ℃ | 207 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 2.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 17300 | MPa | ASTM D790 |
| 23℃ | 19000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 378 | MPa | ASTM D790 |
| 23℃ | 355 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 13 | kJ/m² | ISO 179 |
| 23℃ | 15 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 90 | kJ/m² | ISO 179 |
| 23℃ | 90 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 15 | kJ/m² | ISO 180 |
| 23℃ | 160 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 213 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 214 | ℃ | ISO 75-2/A |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Relative temperature index | |||
| 1.5 mm | 130 | ℃ | UL 746 |
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| 3.0 mm | 130 | ℃ | UL 746 |
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 105 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.12 | % | |
| Barrel rear temperature | 275 to 300 | °C | |
| Barrel middle temperature | 285 to 310 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 300 to 320 | °C | |
| Processing (melt) temperature | 300 to 320 | °C | |
| Mold temperature | 80 to 95 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |