| About |
|---|
| Ultramid B3WG13 HPX BK00102 is a 63% glass reinforced, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldability and outstanding surface appearance.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,Grease resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data |
|---|
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.12 | % | |
| Barrel rear temperature | 275 to 300 | °C | |
| Barrel middle temperature | 285 to 310 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 300 to 320 | °C | |
| Processing (melt) temperature | 300 to 320 | °C | |
| Mold temperature | 80 to 95 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |