| About |
|---|
| Glass fibre reinforced and heat ageing resistant injection moulding grade, with enhanced flowability used e.g. for automobile manifolds&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Good liquidity,Grease resistance |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Volume flow rate of solution | |||
| 275℃/10.0 kg | 55 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.75 | % | ISO 294-4 |
| MD | 0.25 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.3-6.9 | % | ISO 62 |
| Balance, 23 ° C, 50% RH | 1.9-2.3 | % | ISO 62 |
| 96% H2SO4 | 145 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9300 | MPa | ISO 527-2 |
| fracture | 170 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.7 | % | ISO 527-2 |
| Bending modulus | 8700 | MPa | ISO 178 |
| bending strength | 260 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 90 | kJ/m² | ISO 179/1eU |
| -30℃ | 74 | kJ/m² | ISO 179/1eU |
| Izod Notched Impact strength | |||
| -30℃ | 9.6 | kJ/m² | ISO 180/A |
| 23℃ | 16 | kJ/m² | ISO 180/A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 205 | ℃ | ISO 75-2/A |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| MD：23-80℃ | 2.4E-5-2.6E-5 | cm/cm/℃ | ISO 11359-2 |
| TD：23-80℃ | 7.9E-5-1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| specific heat | 1270 | J/kg/℃ | |
| Maximum operating temperature | 200 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 1 MHz | 3.90 | IEC 60250 | |
| 1 MHz | 0.023 | V | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6 mm | HB | IEC 60695-11-10 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 80 | °C | |
| Barrel rear temperature | 260 | °C | |
| Barrel middle temperature | 270 | °C | |
| Barrel front temperature | 280 | °C | |
| Nozzle temperature | 280 | °C | |
| Processing (melt) temperature | 270-290 | °C | |
| Mold temperature | 80-90 | °C | |
| Residence Time | < 10.0 | min | |
| Screw Speed | < 300 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 280°C, TW = 80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |