| About |
|---|
| Ultramid B3ZG8 BK20560 is an impact-modified, pigmented black and 40% glass fiber reinforced injection molding PA6 grade having very high impact strength and rigidity. Applications Typical applications include airbag housings and half-shells for suitcases.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Grease resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 50%RH | 1.6 | % | ISO 62 |
| saturated | 5.0 | % | ISO 62 |
| Volume flow rate of solution | |||
| 235℃，5Kg | 4 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 11600 | MPa | ISO 527 |
| tensile strength | |||
| Fracture, 23 ℃ | 160 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527 |
| Bending modulus | |||
| 23℃ | 9500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180 | ||
| -30℃ | 14 | kJ/m² | ISO 180 |
| 23℃ | 22 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| A，C | 205 | ℃ | ISO 75 |
| B，C | 220 | ℃ | ISO 75 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |