Ultramid® D3WG12 HMG BK00102

About
Ultramid D3WG12 HMG BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid D3WG12 HMG BK00102 shows improved retention of mechanical properties after moisture conditioning. In addition, molded parts possess an exceptional surface finish. Applications Ultramid D3WG12 HMG BK00102 was designed for applications requiring very high rigidity and should be considered for components that are constructed with metal.&&

About

Ultramid D3WG12 HMG BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid D3WG12 HMG BK00102 shows improved retention of mechanical properties after moisture conditioning. In addition, molded parts possess an exceptional surface finish. Applications Ultramid D3WG12 HMG BK00102 was designed for applications requiring very high rigidity and should be considered for components that are constructed with metal.&&

Product Description
Supplier	BASF
Generic	PA66
Material Status	Commercial: Active
Features	Good Rigidity,Good surface appearance
Availabilitys	North America,Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.75	g/cm³
Shrinkage rate
TD	0.25	%
MD	0.19	%
Water absorption rate
Saturation, 23 ℃	2.5	%
Equilibrium, 23 ℃, 50% RH	1.0	%

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	20200	MPa
tensile strength
Fracture, 23 ℃	248	MPa
Tensile strain
Fracture, 23 ℃	2.5	%
Bending modulus
23℃	18900	MPa
bending strength
23℃	383	MPa

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
-30℃	12	kJ/m²
23℃	13	kJ/m²
Charpy Unnotch Impact strength
-30℃	95	kJ/m²
23℃	99	kJ/m²
Impact strength of cantilever beam notch
-40℃	12	kJ/m²
23℃	13	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
1.8 MPa, unannealed	224	℃
Melting temperature
DSC	260	℃

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.15	%
Processing (melt) temperature	280 to 305	°C
Mold temperature	80 to 90	°C
Injection pressure	3.50 to 12.5	MPa
Injection speed	快速

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.