| About |
|---|
| Ultramid Endure D3G7 BK20560 is a glass fiber reinforced injection molding grade with high stiffness, very good flowability, and excellent heat aging resistance up to at least 220 degC (428 degF).&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good heat aging resistance,Good liquidity |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.87 | % | ISO 294-4 |
| MD | 0.30 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| 23℃ | 11300 | MPa | ISO 527-2 |
| 150℃ | 4200 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Fracture, 23 ℃ | 200 | MPa | ISO 527-2 |
| Fracture, 150 ℃ | 84.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Fracture, 23 ℃ | 2.9 | % | ISO 527-2 |
| Fracture, 150 ℃ | 6.7 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 10600 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 11 | kJ/m² | ISO 179 |
| 23℃ | 10 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 60 | kJ/m² | ISO 179 |
| 23℃ | 80 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| TD | 8.0E-5 to 1.3E-4 | 1/℃ | |
| MD | 1.4E-5 to 2.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 3.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 48 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.12 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 90 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |