| About |
|---|
| Ultramid HFX 33 is a polyamide specialty extrusion resin combining high flexibility, excellent burst performance and outstanding chemical resistance. It offers high melt strength and enhanced heat stability. Applications Ultramid HFX 33 is recommended for tubing applications requiring an outstanding balance of flexibility, chemical and heat resistance and burst performance.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good melt strength,Solvent resistance,Heat Stabilized |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 430 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 40.0 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | 300 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 400 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 120 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 90 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 40.0 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 65 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel 1 zone temperature | 225 to 245 | °C | |
| Barrel 3 zone temperature | 225 to 250 | °C | |
| Barrel 5 zone temperature | 225 to 245 | °C | |
| Flange temperature | 230 to 245 | °C | |
| Melt temperature | 225 to 245 | °C | |
| Head temperature | 230 to 245 | °C | |
| Nozzle temperature | 230 to 245 | °C | |
| Extruder screw length to diameter ratio L / D | 20.0:1.0 to 24.0:1.0 | ||
| Extruder screw compression ratio | 3.5:1.0 to 4.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |