| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA 9T |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Halogen free,Mechanical property,Heat Stabilized,Electrical performance,Solvent resistance,Ultra high liquidity,Ultra high toughness,high-rigidity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding shrinkage | |||
| Parallel | 0.35 | % | ISO 294-4 |
| Normal | 0.95 | % | ISO 294-4 |
| Moisture Absorption | |||
| Saturation | 2.0 | % | ISO 62 |
| Melt Volume Rate | |||
| 325℃，5kg | 30 | ccm/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 10500 | MPa | ISO 527 |
| Wet Cond | 10500 | MPa | ISO 527 |
| Tensile Strength | |||
| Broken BRK, dry dry | 140 | MPa | ISO 527-2 |
| Broken BRK, wet Cond | 130 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, dry dry | 2.2 | % | ISO 527 |
| Broken BRK, wet Cond | 2.2 | % | ISO 527 |
| Flexural Strength | |||
| Dry | 220 | MPa | ISO 178 |
| Wet Cond | 210 | MPa | ISO 178 |
| Flexural Modulus | |||
| Dry | 10500 | MPa | ISO 178 |
| Wet Cond | 10500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23 ℃, dry | 7 | kJ/m² | ISO 179 |
| 23 ℃, moist cond | 7 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| -30 ℃, dry | 60 | kJ/m² | ISO 179 |
| 23 ℃, dry | 60 | kJ/m² | ISO 179 |
| 23 ℃, moist cond | 50 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting point | 300 | ℃ | ISO 3146 |
| Hot deformation temperature HDT | 260 | ℃ | ISO 75 |
| Coeff. of linear thermal expansion | |||
| Dry | 2E-5 | mm/mm/℃ | |
| Wet Cond | 5E-5~5.5E-5 | mm/mm/℃ |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared Tracking Index | 600 | IEC 60112 | |
| Volume Resistance | |||
| Dry | 1E15 | ohm·m | IEC 60093 |
| Wet Cond | 1E15 | ohm·m | IEC 60093 |
| Dielectric Constant | |||
| Dry, 1 MHz | 3.7 | IEC 60250 | |
| Wet Cond, 1 MHz | 3.8 | IEC 60250 | |
| Dissipation Factor | |||
| Dry, 1 MHz | 110 | E-4 | IEC 60250 |
| Wet Cond, 1 MHz | 160 | E-4 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.4 mm | V-0 | UL 94 | |
| 0.75 mm | V-0 | UL 94 | |
| 1.5 mm | V-0,5VA | UL 94 | |
| 3.0 mm | V-0,5VA | UL 94 | |
| Relative Temperature Index | |||
| No mechanical w/o impact | |||
| 0.4 mm | 85 | ℃ | UL746B |
| 0.75 mm | 85 | ℃ | UL746B |
| 1.5 mm | 85 | ℃ | UL746B |
| 3.0 mm | 85 | ℃ | UL746B |
| Mechanical w/Impact | |||
| 0.4 mm | 85 | ℃ | UL746B |
| 0.75 mm | 85 | ℃ | UL746B |
| 1.5 mm | 85 | ℃ | UL746B |
| 3.0 mm | 85 | ℃ | UL746B |
| Electrical | |||
| 0.4 mm | 85 | ℃ | UL746B |
| 0.75 mm | 85 | ℃ | UL746B |
| 1.5 mm | 85 | ℃ | UL746B |
| 3.0 mm | 85 | ℃ | UL746B |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 | ℃ | |
| Drying Time | 8 | hr | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 310-340 | ℃ | |
| Mold Temperature | 100-160 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |