Ultramid® S3WG6 PA 610 (Dry)

About
聚合物、热塑性塑料、尼龙、尼龙610、尼龙610、玻璃增强30%,干燥

Product Description
Supplier	BASF
Generic	PA6
Material Status	Commercial: Active
Features	Corrosion Resistant
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.31	g/cm³	ISO 1183
Water absorption rate	2.0 – 2.6	%	ISO 62
Balanced moisture absorption	0.80 – 1.2	%	ISO 62
Viscosity measurement	150		ISO 307
Shrinkage rate	0.40	%	Test Box 1.5 mm
MD	0.90	%	ISO 2577
MD	0.40	%	ISO 2577
Melt Flow Rate
275℃	39.3	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	150	MPa	ISO 527-1-2
Tensile strain
yield	4.0	%	ISO 527-1/2
Elastic modulus	8.40	GPa	ISO 527-1/-2
bending strength	230	MPa	ISO 178
Bending modulus	7900	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
-30℃	8.50	J/cm²	ISO 179/1eU
23℃	9.00	J/cm²	ISO 179/1eU
Charpy Notched Impact Strength
-30℃	0.800	J/cm²	ISO 179/1eA
23℃	1.30	J/cm²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Melting temperature	220	℃	ISO 11357-1/-3
Processing (melt) temperature	270 – 290	℃	注射成型
Mold temperature	80.0 – 90.0	℃	注射成型

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.