| Ultrason E 1010 is an unreinforced, low viscosity injection molding PESU grade. It flows readily and offers outstanding heat resistance and dimensional stability. Applications Typical applications include automotive applications such as fuse encapsulation, connectors, heating system and headlight components and household applications such as microwave dishes and other applications requiring high heat resistance.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Good liquidity,Low Viscosity,High Heat Resistance,V-1,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 360℃，10 kg | 150 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.82 | % | ISO 294-4 |
| MD | 0.79 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 2.2 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.80 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 7.0 | kJ/m² | ISO 179 |
| 23℃ | 6.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | No Break | ISO 179 | |
| 23℃ | No Break | ISO 179 | |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -30℃ | 7.0 | kJ/m² | ISO 180 |
| 23℃ | 6.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 203 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 5.2E-5 | 1/℃ | |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.6 mm | 180 | ℃ | UL 746 |
| 3.0 mm | 180 | ℃ | UL 746 |
| 1.6 mm | 190 | ℃ | UL 746 |
| 3.0 mm | 190 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | 37 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 3.90 | IEC 60250 | |
| 1 MHz | 3.80 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.7E-3 | IEC 60250 | |
| 1 MHz | 0.014 | IEC 60250 | |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2650 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 85.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 6.8 | % | ISO 527-2 |
| Ball hardness | 154 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 150 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 340 to 390 | °C | |
| Mold temperature | 140 to 180 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |