| About |
|---|
| Unreinforced, higher viscosity injection molding and extrusion grade with improved toughness and chemical resistance (stress crack resistance); demolding optimized&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | Good flexibility,High Viscosity,Solvent resistance,V-0 |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume Rate | |||
| 360℃，10 kg | 35.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.90 | % | |
| MD | 0.85 | % | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 2.2 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.80 | % | |
| Viscosity number | 66.0 | cm³/g | ISO 307 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 8.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 207 | ℃ | ISO 75-2/A |
| Glass transition temperature | 228 | ℃ | ISO 11357-2 |
| Linear coefficient of thermal expansion | |||
| MD | |||
| Temperature index | |||
| 23 to 80 ℃ | 5.2E-5 | cm/cm/℃ | ISO 11359-2 |
| At 50% tensile strength loss | 180 | ℃ | IEC 60216 |
| Maximum operating temperature | |||
| 180℃ | 5.9E-5 | cm/cm/℃ | DIN 53752 |
| short cycle operation | 220 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 34 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.80 | ||
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.7E-3 | ||
| 1 MHz | 0.014 | ||
| Compared to the leakage tracing index | IEC 60112 | ||
| Solution A | 100 | V | |
| Solution B | 100 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 154 | MPa | ISO 2039-1 |
| Tensile modulus | 2650 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 85.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.9 | % | ISO 527-2/50 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 140 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 80.0 | °C | |
| Barrel rear temperature | 350 | °C | |
| Barrel middle temperature | 360 | °C | |
| Barrel front temperature | 370 | °C | |
| Nozzle temperature | 370 | °C | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 140 to 180 | °C | |
| Screw Speed | mm/sec | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 3. 10°C/min |
| 4. 20000 h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |