| About |
|---|
| Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibres, graphite and PTFE powder, considerably improves Ultrason tribological properties. In addition, this product has a very small expansion coefficient and low tendency to swell in hot oils.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PES |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume Rate | |||
| 360℃，10 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.46 | % | ISO 294-4 |
| MD | 0.31 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 1.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.50 | % | ISO 62 |
| Viscosity number | 56.0 | cm³/g | ISO 307 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 20 | kJ/m² | ISO 179/1eU |
| 23℃ | 24 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 5.5 | kJ/m² | ISO 180-A |
| 23℃ | 6.5 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 223 | ℃ | ISO 75-2/A |
| Glass transition temperature | 225 | ℃ | ISO 11357-2 |
| Linear coefficient of thermal expansion | |||
| MD | |||
| 23 to 80 ℃ | 1.1E-5 | cm/cm/℃ | ISO 11359-2 |
| 180℃ | 1.3E-5 | cm/cm/℃ | DIN 53752 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 4.0E+3 | ohms | IEC 60093 |
| Volume resistivity | 9.0E+5 | ohms·cm | IEC 60093 |
| Dielectric strength | 8.0 | kV/mm | IEC 60243-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H 961/30 | 180 | MPa | ISO 2039-1 |
| Tensile modulus | 11000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 115 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.5 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 140 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 80 | °C | |
| Barrel rear temperature | 350 | °C | |
| Barrel middle temperature | 360 | °C | |
| Barrel front temperature | 370 | °C | |
| Nozzle temperature | 370 | °C | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 150 to 190 | °C | |
| Screw Speed | < 300 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |