| About |
|---|
| KEY FEATURES UmaPET HSCO is transparent film with one side heat sealable Co-extruded layer of special copolymer and other side corona treated. Corona treated side gives enhanced adhesion for printing and lamination. The special copolymer layer is design to heat seal onto itself as well as substrates such as APET, C-PET, Modified C-PET and A-PET coated boards. The film has excellent transparency, dimensional stability and barrier. The Film can be used for direct contact with food and complies with FDA regulation 21CFR177.1630 sections (f) and (g). APPLICATIONS Excellent in flexible packaging applications as sealant for products which need high aroma barrier like perfumed tissues, mosquito mats etc. Suitable for used in monolayer over wrap, temper evident packaging. Suitable for sealing cap liner for PET jars, see through lid for preformed PET trays, microoven able pouches for sandwich.&& |
| Product Description | |
|---|---|
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good heat sealing,Good Dimensional Stability,Food contact compliance,Good bond,Copolymer |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | ASTM D1204 | ||
| MD：150℃，0.012 mm，30 min | 2.5 | % | |
| MD：150℃，0.015 mm，30 min | 2.5 | % | |
| MD：150℃，0.02 mm，30 min | 2.0 | % | |
| MD：150℃，0.025 mm，30 min | 2.0 | % | |
| TD：150℃，0.012 mm，30 min | 0.40 | % | |
| TD：150℃，0.015 mm，30 min | 0.40 | % | |
| TD：150℃，0.02 mm，30 min | 0.40 | % | |
| TD：150℃，0.025 mm，30 min | 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.40 | ||
| With oneself – dynamic | 0.40 | ||
| With oneself – dynamic | 0.40 | ||
| With oneself – dynamic | 0.38 | ||
| With oneself – static | 0.48 | ||
| With oneself – static | 0.48 | ||
| With oneself – static | 0.48 | ||
| With oneself – static | 0.48 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 12 15 20 25 | µm | |
| film thickness | 12, 15, 20, 25 µm | ||
| tensile strength | ASTM D882 | ||
| MD, fracture, 12 µ m | 177 | MPa | |
| MD, fracture, 15 µ m | 177 | MPa | |
| MD, fracture, 20 µ m | 172 | MPa | |
| MD, fracture, 25 µ m | 172 | MPa | |
| TD, fracture, 12 µ m | 186 | MPa | |
| TD, fracture, 15 µ m | 186 | MPa | |
| TD, fracture, 20 µ m | 181 | MPa | |
| TD, fracture, 25 µ m | 181 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 12 µ m | 100 | % | |
| MD, fracture, 15 µ m | 100 | % | |
| MD, fracture, 20 µ m | 100 | % | |
| MD, fracture, 25 µ m | 100 | % | |
| TD, fracture, 12 µ m | 90 | % | |
| TD, fracture, 15 µ m | 90 | % | |
| TD, fracture, 20 µ m | 90 | % | |
| TD, fracture, 25 µ m | 90 | % | |
| dosage | Internal Method | ||
| 12.0 µm | 59.5 | m²/kg | |
| 15.0 µm | 47.6 | m²/kg | |
| 20.0 µm | 35.7 | m²/kg | |
| 25.0 µm | 28.6 | m²/kg |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 12 µm | 3.0 | % | |
| 15 µm | 3.0 | % | |
| 20 µm | 3.5 | % | |
| 25 µm | 4.0 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Wetting Tension | ASTM D2578 | ||
| Corona side：12.0 µm | 52 | dyne/cm | |
| Corona side：15.0 µm | 52 | dyne/cm | |
| Corona side：20.0 µm | 52 | dyne/cm | |
| Corona side：25.0 µm | 52 | dyne/cm | |
| Plain side：12.0 µm | 44 | dyne/cm | |
| Plain side：15.0 µm | 44 | dyne/cm | |
| Plain side：20.0 µm | 44 | dyne/cm | |
| Plain side：25.0 µm | 44 | dyne/cm |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |