| KEY FEATURES UmaPET ITM is medium barrier, isotropic metallized film. It exhibits excellent isotropic balanced mechanical properties along with superior barrier and good metal to film bond strength/adhesion. It has excellent mechanical properties, flex crack resistance and excellent gloss. APPLICATIONS UmaPET ITM is used as barrier layer in form of lidding in flexible packaging applications which require good barrier and high bond strength in laminates. Typical usage as lidding film in yogurt, milk, flavored dairy products, cakes, chocolates and other cup packed products.&& |
| Product Description | |
|---|---|
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good bond,Good tear strength,Electroplating,Block resin,Agglomerability |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | ASTM D1204 | ||
| MD：150℃，0.012 mm，30 min | 2.2 | % | |
| MD：150℃，0.023 mm，30 min | 2.2 | % | |
| TD：150℃，0.012 mm，30 min | 0.0 | % | |
| TD：150℃，0.023 mm，30 min | 0.0 | % | |
| Surface tension – Metallized side | ASTM D2578 | ||
| 12.0 µm | 56 | mN/m | |
| 23.0 µm | 56 | mN/m | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 12 23 | µm | |
| film thickness | 12, 23 µm | ||
| tensile strength | ASTM D882 | ||
| MD, fracture, 12 µ m | 216 | MPa | |
| MD, fracture, 23 µ m | 196 | MPa | |
| TD, fracture, 12 µ m | 226 | MPa | |
| TD, fracture, 23 µ m | 206 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 12 µ m | 100 | % | |
| MD, fracture, 23 µ m | 100 | % | |
| TD, fracture, 12 µ m | 95 | % | |
| TD, fracture, 23 µ m | 95 | % | |
| Oxygen permeability | ASTM D3985 | ||
| 23℃，12 µm | < 0.800 | cm³/m²/24 hr | |
| 23℃，23 µm | < 0.700 | cm³/m²/24 hr | |
| Water vapor permeability | ASTM F1249 | ||
| — | < 0.60 | g/m²/24 hr | |
| — | < 0.70 | g/m²/24 hr | |
| dosage | Internal Method | ||
| 12.0 µm | 59.5 | m²/kg | |
| 23.0 µm | 31.0 | m²/kg |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Optical Density | Internal Method | ||
| 12.0 µm | -2.8 to 7.2 | % | |
| 23.0 µm | -2.8 to 7.2 | % |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |