UmaPET MHLO - SOLIAO

About
KEY FEATURES UmaPET MHLO film is medium Haze, medium gloss film with excellent muted and grainy surface with one side chemically primed for improved adhesion performance. The film exhibits excellent thermal, mechanical and matte surface properties along with excellent dimensional stability and excellent process ability. After metallization, shows silver finish as aesthetic. APPLICATIONS The film is widely used for label face stocks, carrier for thermal transfer printing, hot stamping, paper board and carton lamination applications. Chemical coated surface gives enhanced adhesion performance to inks, adhesives and other primer coatings and metal in metallization. Metallized films can be used as label face stocks and sandwich barrier layer which showssilver aesthetic appearance to the package in flexible packaging.&&

About

KEY FEATURES UmaPET MHLO film is medium Haze, medium gloss film with excellent muted and grainy surface with one side chemically primed for improved adhesion performance. The film exhibits excellent thermal, mechanical and matte surface properties along with excellent dimensional stability and excellent process ability. After metallization, shows silver finish as aesthetic. APPLICATIONS The film is widely used for label face stocks, carrier for thermal transfer printing, hot stamping, paper board and carton lamination applications. Chemical coated surface gives enhanced adhesion performance to inks, adhesives and other primer coatings and metal in metallization. Metallized films can be used as label face stocks and sandwich barrier layer which showssilver aesthetic appearance to the package in flexible packaging.&&

Product Description
Generic	PET
Material Status	Commercial: Active
Features	Excellent Processability,Good Dimensional Stability,Good Printability,Good bond,Electroplating
Availabilitys	Africa & Middle East ,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate			ASTM D1204
MD：150℃，0.012 mm，30 min	2.0	%
TD：150℃，0.012 mm，30 min	0.40	%

MECHANICAL	Nominal value	Test method
friction coefficient		ASTM D1894
With oneself – dynamic	0.38
With oneself – static	0.45

film	Nominal value	Unit	Test method
film thickness
test	12	µm
film thickness	12 µm
tensile strength			ASTM D882
MD, fracture, 12 µ m	186	MPa
TD, fracture, 12 µ m	196	MPa
Tensile strain			ASTM D882
MD, fracture, 12 µ m	90	%
TD, fracture, 12 µ m	85	%
dosage
12.0 µm	59.5	m²/kg	Internal Method

optical performance	Nominal value	Unit	Test method
gloss
60°	48		ASTM D2457
Haze
12 µm	44	%	ASTM D1003

Supplementary information	Nominal value	Unit	Test method
Wetting Tension（Coated side，12.0 µm）	48	dyne/cm	ASTM D2578

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.