| About |
|---|
| UMG ABS® GF10是一种丙烯腈丁二烯苯乙烯(ABS)材料,含有的填充物为10% 玻璃纤维增强材料。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 UMG ABS® GF10的主要特性有: 阻燃/额定火焰 通过 ROHS 认证&& |
| Product Description | |
|---|---|
| Supplier | Techno |
| Generic | ABS |
| Material Status | Commercial: Negative |
| Features | HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：23℃ | 0.20 to 0.40 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 3.0 | kJ/m² | ISO 179 |
| 23℃ | 7.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 98.0 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD | 5.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ISO 2039-2 | |
| Tensile modulus | |||
| 23℃ | 4800 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 83.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 4200 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 116 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 190 to 210 | °C | |
| Barrel middle temperature | 210 to 230 | °C | |
| Barrel front temperature | 220 to 250 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Injection pressure | 70.0 to 140 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |