| About |
|---|
| Product Description | |
|---|---|
| Supplier | Techno |
| Generic | PC+PS |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃ | 27 | cm³/10min | ISO 1133 |
| Shrinkage rate | 1.5 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8800 | MPa | ISO 527 |
| tensile strength | 100 | MPa | |
| Bending modulus | 9000 | MPa | ISO 178 |
| bending strength | 150 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 122 | ISO 2039 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 98 | ℃ | ISO 75 |
| Linear coefficient of thermal expansion | 1.5×10^-5 | cm/cm/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.40 mm | HB*BK | UL 94 | |
| 0.80-3.00 mm | V-0 | UL 94 | |
| 1.70-3.00 mm | 5VB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Dry conditions | Nominal value | Unit | Test method |
| Nozzle temperature | 240~260 | ℃ | |
| Front temperature | 250~270 | ℃ | |
| Mid section temperature | 240~260 | ℃ | |
| Post stage temperature | 220~240 | ℃ | |
| Melt Temperature | 250~270 | ℃ | |
| Injection pressure | 70~140 | MPa | |
| Injection speed | 高速 | ||
| Screw speed | 40~60 | rpm | |
| Back pressure | 5~15 | MPa | |
| Mold temperature | 60~80 | ℃ | |
| drying temperature | 90~105 | ℃ | |
| Drying time | 3~4 | hrs | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |