| About |
|---|
| UMG WOOD® W305A是一种丙烯腈-苯乙烯-丙烯酸酯 (ASA)材料,。 该产品在北美洲或亚太地区有供货,。 UMG WOOD® W305A的主要特性为:通过 ROHS 认证。&& |
| Product Description | |
|---|---|
| Supplier | Techno |
| Generic | ASA |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃ | 27.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2350 | MPa | ISO 527 |
| tensile strength | 39.0 | MPa | ISO 527 |
| Bending modulus | 2550 | MPa | ISO 178 |
| bending strength | 64.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 98 | ISO 2039 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 3.0 | kJ/m² | ISO 179 |
| 23℃ | 4.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 80.0 | ℃ | ISO 75 |
| Linear coefficient of thermal expansion | 8.0×10^-5 | cm/cm/℃ | ISO 11359-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |