UNITHENE® LH901

About
UNITHENE LH901 is a high density polyethylene (HDPE) especially used for the extrusion of filament and sheet. A combination of excellent stretchability, less melt fracture, high tenacity and good processability makes it be suitably tailored for the fabrication of fishing nets, ropes, windows screen, upholstery, filters, woven sacks, canvas laminated cloth and various other industrial and ornamental knitted items. In addition, it can be applied to the manufacture of sheet, thin film and molded articles with good resistance to stress cracking. UNITHENE LH901 can be easily pigmented to any color by either dry blending or melt blending of the masterbatch into the resin.&&

About

UNITHENE LH901 is a high density polyethylene (HDPE) especially used for the extrusion of filament and sheet. A combination of excellent stretchability, less melt fracture, high tenacity and good processability makes it be suitably tailored for the fabrication of fishing nets, ropes, windows screen, upholstery, filters, woven sacks, canvas laminated cloth and various other industrial and ornamental knitted items. In addition, it can be applied to the manufacture of sheet, thin film and molded articles with good resistance to stress cracking. UNITHENE LH901 can be easily pigmented to any color by either dry blending or melt blending of the masterbatch into the resin.&&

Product Description
Supplier	USI
Generic	HDPE
Material Status	Commercial: Active
Features	Excellent Processability,Good Tensile Strength,High density,High ESCR,Good coloring
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.953	g/cm³	ASTM D1505
Melt Flow Rate	0.95	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	540	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -76.0	℃	ASTM D746
Vicat Softening Temp	125	℃	ASTM D1525
Melting peak temperature	131	℃	ASTM D3418

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	68		ASTM D2240
Tensile modulus
1% cut, molded	726	MPa	ASTM D638
tensile strength			ASTM D638
yield	24.5	MPa	ASTM D638
fracture	29.4	MPa	ASTM D638
Tensile strain
fracture	1100	%	ASTM D638
Bending modulus
23℃	1080	MPa	ASTM D747

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.