| UNITIKA Nylon 66 B2040G33 is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in Asia Pacific or North America. Typical applications include: Electrical/Electronic Applications Automotive&& |
| Product Description | |
|---|---|
| Supplier | UNITIKA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 | % | ISO 294-4 |
| TD：3.2 mm | 0.80 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，50% RH | 1.70 | % | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 230 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD | 4.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+14 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 1.00 mm | 35 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 23℃ | 3.50 | 1 MHz | IEC 60250 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 75 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 120 | R 级 | ISO 2039-2 |
| tensile strength | |||
| 23℃ | 170 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 1000 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 260 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 9000 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion molding conditions | Nominal value | Unit | Test method |
| Die temperature | 150-180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |