Urochem 134 - SOLIAO

About
Urea- formaldehyde resins with melamine resin fortified with highly refined cellulose as filler, and further modified with minor amounts of special purpose additives, pigments, cure regulators and lubricants. The Urochem 134 Moulding Compounds can be supplied in an almost unlimited range of colours from translucent light pastels to black. Moulded parts are free from odour; UV stable with good moisture resistance. Hard, glossy and scratch resistant surface. Excellent chemical resistance. Fats, oils and common organic solvents like alcohol and acetone do not attack moulded parts which are also resistant to surfactants and weak bases. They will withstand attack from weak acids for a shorter duration. Excellent electrical properties (arc quenching, tracking, flame resistance). Oxygen index of 30% is achieved without the use of external flame retardants. No halogens are present in the composition. Compliant with the requirements of widely used material specifications for amino compounds: BS 1322 type UF A10 () DIN 7708 type 131.5 () ISO 2112 type UF A10 () UL certified () included in ISO 14527 Fields of application: Optimized for use primarily in the thermoset injection moulding process. Particularly well suited for electrical components such as sockets, lamp holders, and domestic circuit breakers.&&

About

Urea- formaldehyde resins with melamine resin fortified with highly refined cellulose as filler, and further modified with minor amounts of special purpose additives, pigments, cure regulators and lubricants. The Urochem 134 Moulding Compounds can be supplied in an almost unlimited range of colours from translucent light pastels to black. Moulded parts are free from odour; UV stable with good moisture resistance. Hard, glossy and scratch resistant surface. Excellent chemical resistance. Fats, oils and common organic solvents like alcohol and acetone do not attack moulded parts which are also resistant to surfactants and weak bases. They will withstand attack from weak acids for a shorter duration. Excellent electrical properties (arc quenching, tracking, flame resistance). Oxygen index of 30% is achieved without the use of external flame retardants. No halogens are present in the composition. Compliant with the requirements of widely used material specifications for amino compounds: BS 1322 type UF A10 (*) DIN 7708 type 131.5 (*) ISO 2112 type UF A10 (*) UL certified (*) included in ISO 14527 Fields of application: Optimized for use primarily in the thermoset injection moulding process. Particularly well suited for electrical components such as sockets, lamp holders, and domestic circuit breakers.&&

Product Description
Generic	脲醛树脂
Material Status	Commercial: Active
Features	Weather resistance is good,Alkali resistant,Good surface appearance,Good Electrical Properties,Renewable resources,Ethanol tolerance,Good Hardness,Halogen free,Low odor,Moisture resistance,Lubricating,Grease resistance,Solvent resistance,High scratch resistance,V-0
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.50	g/cm³	ISO 1183
Shrinkage rate			ISO 2577
—	0.80 to 1.0	%	ISO 2577
—	0.80 to 1.1	%	ISO 2577
Water absorption rate	< 200.0	mg	ISO 62

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	> 55.0	MPa	ISO 527-2
bending strength	> 100	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	> 1.6	kJ/m²	ISO 179-1eA
Charpy Unnotch Impact strength	> 8.0	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	> 130	℃	ISO 75-2/A
8.0 MPa, unannealed	> 90.0	℃	ISO 75-2/C

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	> 1.1E+11	ohms	IEC 60093
Volume resistivity	> 1.1E+11	ohms·cm	IEC 60093
Dielectric constant	5.00		DIN 53483
Compared to the leakage tracing index	> 600	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	V-0		UL 94
Glowing wire flammability index	960	℃	IEC 707
Extreme oxygen index	> 30	%	ASTM D2863

Process Conditions
injection	Nominal value	Unit	Test method
Nozzle temperature	95 to 115	°C
Mold temperature	145 to 160	°C
Injection pressure	70.0 to 150	MPa
Hold pressure	30.0 to 80.0	MPa
Back pressure	10.0 to 14.0	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
2. Post-shrink
3. 180 sec
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.