| About |
|---|
| Utomer Polyether type TPU which can be applied to Injection, Extrusion and Calendering. Molding cycle is short and efficient for Injection production. The stability melt is easy for Extrusion production. Hydrolysis resistance, low temperature performance with a wide processing window. Extrusion Blown, Flat Die Cast Film, Injection Tag Wheel and Cable Jacketing&& |
| Product Description | |
|---|---|
| Supplier | Utomer |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Low contractility,Good tear strength |
| Availabilitys | North America |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| 100% strain | 7.00 | MPa | ASTM D412 |
| 300% strain | 17.0 | MPa | ASTM D412 |
| tensile strength | 28.0 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 550 | % | ASTM D412 |
| tear strength | 0.100 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，70 hr | 28 | % | ASTM D395B |
| 70℃，24 hr | 35 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -50.0 | ℃ | ASTM D3418 |
| Melting temperature | 185 to 200 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 83 to 87 | ASTM D2240 | |
| Wear amount | 25.0 | mm³ | DIN 53516 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |