| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Renewable resources,V-0,Resistance to detergents,Heat Stabilized |
| Availabilitys | Asia Pacific,Europe,Africa & Middle East |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.54 | g/cm³ | ASTM D792 |
| Specific volume | 0.650 | cm³/g | ASTM D792 |
| Melt Flow Rate | |||
| 266℃，5.0kg | 81 | g/10min | ASTM D1238 |
| Shrinkage rate | Internal Method | ||
| MD | 0.60 to 0.90 | % | |
| MD | 0.40 to 0.60 | % | |
| TD | 0.50 to 0.80 | % | |
| TD | 0.80 to 1.1 | % | |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 320 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 204 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 188 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | ASTM E831 | ||
| -40 to 40 ℃ | 4.5E-5 | cm/cm/℃ | |
| 60 to 138 ℃ | 6.1E-5 | cm/cm/℃ | |
| Relative temperature index | 125 | ℃ | UL 746 |
| Electrical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 110 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 4.5E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| 1.6 mm in oil | 22 | kV/mm | |
| 3.2 mm in air | 20 | kV/mm | |
| Dielectric constant | ASTM D150 | ||
| 100 Hz | 3.50 | ||
| 1 MHz | 3.40 | ||
| Dissipation factor | ASTM D150 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 | ||
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.47 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 | |
| tensile strength | |||
| fracture | 89.6 | MPa | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 4830 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 138 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 12 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Suggested injection volume | 40 to 80 | % | |
| Temperature at the rear of the barrel | 238 to 254 | °C | |
| Temperature in the middle of the barrel | 243 to 260 | °C | |
| Front temperature of material barrel | 249 to 266 | °C | |
| Nozzle temperature | 243 to 260 | °C | |
| Processing (melt) temperature | 249 to 266 | °C | |
| Mold temperature | 65.6 to 87.8 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 50 to 80 | rpm | |
| Exhaust hole depth | 0.025 to 0.038 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |