| About |
|---|
| 30% 玻纤增强PBT+PET 共混物。颜色稳定。阻燃。家电用具：烫斗边缘、烤箱外表/面板 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PBT+PET |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Good color stability |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Yield, Type I, 5 mm/min | 108 | MPa | ASTM D638 |
| Fracture, Type I, 5 mm/min | 110 | MPa | ASTM D638 |
| Tensile strain | |||
| Type I, 5 mm/min | 3.1 | % | ASTM D638 |
| Tensile modulus | |||
| 5 mm/min | 6200 | MPa | ASTM D638 |
| bending strength | |||
| Fracture, 50 mm span | 155 | MPa | ASTM D790 |
| Bending modulus | |||
| 8270 | MPa | ASTM D790 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam at 23 ℃ | |||
| No gap | 534 | J/m | ASTM D 4812 |
| Gap | 80 | J/m | ASTM D 256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| Unannealed, 6.4 mm | |||
| Relative temperature index | |||
| 0.45 MPa | 212 | ℃ | ASTM D 648 |
| Electrical performance | 130 | ℃ | UL 746B |
| 1.8MPa | 187 | ℃ | ASTM D 648 |
| Impact mechanical performance | 130 | ℃ | UL 746B |
| Non mechanical impact performance | 140 | ℃ | UL 746B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.73 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| 3.2 mm | |||
| Melt Flow Rate | |||
| 266℃，5.0kg | 45 | g/10min | ASTM D1238 |
| MD | 0.2-0.3 | % | SABIC Method |
| TD | 0.5-0.6 | % | SABIC Method |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | |||
| Tungsten wire | 5 | PLC Code | ASTM D495 |
| Hot wire ignition {PLC} | 0 | PLC Code | UL 746A |
| High voltage arc marking rate {PLC} | 4 | PLC Code | UL 746A |
| High current arc ignition (surface {PLC}) | 0 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 3 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.76 mm | V-0 | UL 94 | |
| 2.99 mm | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Drying temperature | 60 – 75 | °C | |
| Drying time | 4 – 5 | hrs | |
| Drying time (gradually increasing) | 8 | hrs | |
| Maximum water content | 0.05 | % | |
| Minimum moisture content | 0.02 | % | |
| Melt temperature | 255 – 275 | °C | |
| Nozzle temperature | 255 – 270 | °C | |
| Front temperature | 255 – 265 | °C | |
| Mid section temperature | 250 – 260 | °C | |
| Post stage temperature | 245 – 255 | °C | |
| Mold temperature | 65 – 95 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 50 – 80 | rpm | |
| Shooting cylinder size | 40 – 80 | % | |
| Depth of exhaust groove | 0.025 – 0.038 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |