VALOX™ FR Resin 420SE0

About
30% glass reinforced, UL94 V-0/5V rated. Numerous applications: edge trimmers, food mixer motor stator and commutator, cooling fan, connectors, bobbins, switches etc&&

Product Description
SupplierSABIC
Genericpolybutylene terephthalate
Material StatusCommercial: Active
FeaturesV-0,5VA,V-2
AvailabilitysNorth America,Europe,Asia Pacific
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.63g/cm³ASTM D792
Specific volume0.610cm³/gASTM D792
Density1.63g/cm³ISO 1183
Melt Flow Rate
250℃，5.0kg42g/10minASTM D1238
Melt Volume Rate
250℃，5 kg29.0cm³/10minISO 1133
Shrinkage rate Internal Method
On the stretching rod, MD0.10 to 0.50%Internal Method
MD：3.2 mm0.50 to 0.70%Internal Method
On the stretching rod, TD0.40 to 0.80%Internal Method
TD：3.2 mm0.50 to 1.0%Internal Method
Water absorption rate
Saturation, 23 ℃0.090%ISO 62
Equilibrium, 23 ℃, 50% RH0.070%ISO 62
Weathering resistancef2 UL 746C

IMPACTNominal valueUnitTest method
Charpy Notched Impact Strength ISO 179/1eA
-30℃6.0kJ/m²ISO 179/1eA
23℃7.0kJ/m²ISO 179/1eA
Charpy Unnotch Impact strength ISO 179/1eU
-30℃50kJ/m²ISO 179/1eU
23℃50kJ/m²ISO 179/1eU
Impact strength of cantilever beam notch ASTM D256
-30℃57J/mASTM D256
23℃60J/mASTM D256
Impact strength of cantilever beam notch ISO 180/1A
23℃620J/mASTM D4812
-30℃6.0kJ/m²ISO 180-1A
23℃7.0kJ/m²ISO 180-1A
Notched impact strength of cantilever beam ISO 180/1U
-30℃45kJ/m²ISO 180/1U
23℃45kJ/m²ISO 180/1U
Dart impact equipped with measuring instruments
23℃，Total Energy5.00JASTM D3763

THERMALNominal valueUnitTest method
Hot deformation temperature 
1.8 MPa, unannealed, 3.2 mm200℃ASTM D648
0.45 MPa, unannealed, 3.2 mm212℃ASTM D648
0.45 MPa, unannealed, 100 mm span220℃ISO 75-2/Be
1.8 MPa, unannealed, 100 mm span195℃ISO 75-2/Ae
1.8 MPa, unannealed, 64 mm span200℃ISO 75-2/Af
Vicat Softening Temp200℃ASTM D1525 11
Vicat Softening Temp 
A50220℃ISO 306/A50
B50200℃ISO 306
B120200℃ISO 306/B120
Ball pressure test
125℃Pass IEC 60695-10-2
Linear coefficient of thermal expansion
TD：-40~40℃8.9E-51/℃ASTM E831
TD ISO 11359-2
-40 to 40 ℃8.9E-5cm/cm/℃ISO 11359-2
23 to 80 ℃1.2E-4cm/cm/℃ISO 11359-2
MD：-40~40℃2.5E-51/℃ASTM E831
MD ISO 11359-2
-40 to 40 ℃2.5E-5cm/cm/℃ISO 11359-2
23 to 80 ℃2.5E-5cm/cm/℃ISO 11359-2
Thermal conductivity coefficient0.25W/m/KISO 8302
Relative temperature index
Electrical performance130℃UL 746
Strength mechanical performance140℃UL 746
Impact mechanical performance130℃UL 746

Electrical performanceNominal valueUnitTest method
Surface resistivity> 1.0E+15ohmsIEC 60093
Volume resistivity> 1.0E+15ohms·cmASTM D257
Volume resistivity> 1.0E+15ohms·cmIEC 60093
Dielectric strength ASTM D149
1.6 mm in oil24kV/mmASTM D149
3.2 mm in air19kV/mmASTM D149
Dielectric strength IEC 60243-1
0.8 mm in oil23kV/mmIEC 60243-1
1.6 mm in oil22kV/mmIEC 60243-1
3.2 mm in oil16kV/mmIEC 60243-1
Dielectric constant ASTM D150
100 Hz3.80 ASTM D150
1 MHz3.70 ASTM D150
Relative permittivity IEC 60250
50 Hz3.30 IEC 60250
60 Hz3.30 IEC 60250
100 Hz3.80 IEC 60250
1 MHz3.30 IEC 60250
Dissipation factor ASTM D150
100 Hz2.0E-3 ASTM D150
1 MHz0.020 ASTM D150
Dissipation factor IEC 60250
50 Hz1.0E-3 IEC 60250
60 Hz1.0E-3 IEC 60250
100 Hz2.0E-3 IEC 60250
1 MHz0.010 IEC 60250
Arc resistancePLC 6 ASTM D495
Compared to the leakage tracing indexPLC 3 UL 746
Compared to the leakage tracing index IEC 60112
CTI175VIEC 60112
Solution B125VIEC 60112
High Arc Burning Index (HAI)PLC 0 UL 746
High voltage arc marking rate
HVTRPLC 4 UL 746
Hot wire ignition
HWIPLC 2 UL 746

FLAME CHARACTERISTICSNominal valueUnitTest method
Flame retardant level UL 94
0.40 mmV-2 UL 94
0.71 mmV-0 UL 94
2.00 mm5VA UL 94
Glowing wire flammability index
1.0 mm960℃IEC 60695-2-12
Extreme oxygen index32%ISO 4589-2

MECHANICALNominal valueUnitTest method
Tensile modulus12000MPaASTM D638
Tensile modulus10000MPaISO 527-1-2
tensile strength
fracture120MPaISO 527-2/5
fracture120MPaASTM D638
yield120MPaISO 527-2/5
yield120MPaASTM D638
Tensile strain
fracture1.9%ISO 527-2/5
fracture2.0%ASTM D638
yield1.9%ISO 527-2/5
yield2.0%ASTM D638
Bending modulus9500MPaISO 178
50 mm span9800MPaASTM D790
bending strength180MPaISO 178
Fracture, 50 mm span186MPaASTM D790
Taber abraser
1000 cycles, 1000 g, CS-17 wheels22.0mgInternal Method
Rockwell hardness
R-level119 ISO 2039-2
R-level119 ASTM D785
Ball hardness
H358/30118MPaISO 2039-1

Process Conditions
InjectionNominal valueUnitTest method
drying temperature121°C
Drying time3.0 to 4.0hr
Drying time, maximum12hr
Recommended maximum moisture content0.020%
Suggested injection volume40 to 80%
Temperature at the rear of the barrel243 to 266°C
Temperature in the middle of the barrel249 to 271°C
Front temperature of material barrel254 to 277°C
Nozzle temperature249 to 271°C
Processing (melt) temperature254 to 277°C
Mold temperature66 to 88°C
Back pressure0.345 to 0.689MPa
Screw speed50 to 80rpm
Exhaust hole depth0.025 to 0.038mm

Notes
1. Typical properties: these are not to be construed as specifications.
2. Tensile Bar
3. 0.20 in/min
4. Type I, 0.20 in/min
5. 0.051 in/min
6. 0.079 in/min
7. 80*10*4 sp=62mm
8. 80*10*4 mm
9. 120*10*4 mm
10. Rate A (50°C/h), Loading 2 (50 N)
11. Tungsten Electrode
12. Surface
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.