| 30% glass fiber reinforced, thin wall brominated FR, high flow, high CTI&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | High liquidity,Flame Characteristics,Bromination |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.67 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 250℃，5 kg | 28.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.30 | % | |
| TD | 0.70 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.24 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 10500 | MPa | ASTM D638 |
| — | 10700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 125 | MPa | ASTM D638 |
| yield | 126 | MPa | ISO 527-2/5 |
| fracture | 125 | MPa | ASTM D638 |
| fracture | 126 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 2.2 | % | ASTM D638 |
| yield | 2.2 | % | ISO 527-2/5 |
| fracture | 2.2 | % | ASTM D638 |
| fracture | 2.2 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 9500 | MPa | ASTM D790 |
| — | 9500 | MPa | ISO 178 |
| bending strength | |||
| — | 190 | MPa | ISO 178 |
| Fracture, 50 mm span | 188 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 8.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 45 | kJ/m² | ISO 179/2U |
| Impact strength of cantilever beam notch | |||
| -30℃ | 77 | J/m | ASTM D256 |
| 23℃ | 76 | J/m | ASTM D256 |
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 740 | J/m | ASTM D4812 |
| 23℃ | 38 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 209 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 211 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 207 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 202 | ℃ | ISO 306 |
| Ball pressure test | |||
| 190℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 2.1E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 1.9E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 1.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.1E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| TD：-40℃ | 7.1E-5 | 1/℃ | ISO 11359-2 |
| TD：23~80℃ | 1.2E-4 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 140 | ℃ | UL 746 |
| Electrical performance | 140 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.6E+16 | ohms | ASTM D257 |
| Volume resistivity | 2.2E+15 | ohms·cm | ASTM D257 |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.28 mm | V-0 | ||
| 1.50 mm | 5VA | ||
| Glowing wire flammability index | |||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 0.4 mm | 775 | ℃ | |
| 0.8 mm | 725 | ℃ | |
| 1 mm | 700 | ℃ | |
| 2 mm | 725 | ℃ | |
| 3 mm | 775 | ℃ | |
| Extreme oxygen index | 30 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 245 to 265 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 255 to 275 | °C | |
| Nozzle temperature | 250 to 270 | °C | |
| Processing (melt) temperature | 255 to 275 | °C | |
| Mold temperature | 65 to 90 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 50 to 80 | rpm | |
| Vent depth | 0.025 to 0.038 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Internal Method |
| 3. 0.20 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Break |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 10. Approximate Maximum |
| 11. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |