| About |
|---|
| VALOX V3504 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0,5VA |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 8.00 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 57.0 | MPa | Internal Method |
| yield | 58.0 | MPa | ASTM D638 |
| yield | 58.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 7.0 | % | ASTM D638 |
| fracture | 16 | % | Internal Method |
| fracture | 9.0 | % | ASTM D638 |
| fracture | 8.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2620 | MPa | ASTM D790 |
| — | 2600 | MPa | ISO 178 |
| bending strength | |||
| — | 88.0 | MPa | ISO 178 |
| Yield, 50 mm span | 90.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 52 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 106 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 80.0 | ℃ | ISO 75-2/Af |
| Relative temperature index | 140 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc ignition resistance index (HVAR) (PLC) | PLC 6 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.38 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glowing wire flammability index | |||
| 0.38 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.4 mm | 825 | ℃ | |
| 1 mm | 825 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended injection volume | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 12 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 232 to 249 | °C | |
| Barrel middle temperature | 238 to 254 | °C | |
| Barrel front temperature | 243 to 260 | °C | |
| Nozzle temperature | 238 to 254 | °C | |
| Processing (melt) temperature | 243 to 260 | °C | |
| Mold temperature | 48.9 to 76.7 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Vent depth | 0.013 to 0.025 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |