VALOX™ V9290 resin

About
45％GF PET，玻璃，脱模，热稳定

Product Description
Supplier	SABIC
Generic	polybutylene terephthalate
Material Status	Commercial: Active
Features	Good flexibility,Good surface appearance,Good Dimensional Stability,Fatigue resistance

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 5 mm/min	160	MPa	ISO 527
tensile strength
Fracture, 5 mm/min	160	MPa	ISO 527
Tensile strain
Yield, 5 mm/min	1.5	%	ISO 527
Tensile strain
Fracture, 5 mm/min	1.5	%	ISO 527
Tensile modulus
1 mm/min	15000	MPa	ISO 527
bending strength
Yield, 2 mm/min	225	MPa	ISO 178
Bending modulus
2 mm/mim	13000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，80104	10	kJ/m²	ISO 180-1A
Impact strength of cantilever beam notch
-30℃，80103	8	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
23 ℃, 80 * 10 * 4, 64mm span	7	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Linear coefficient of thermal expansion
MD：-23~40℃	2.E-05	1/℃	ISO 11359-2
TD：-23~40℃	8.E-05	1/℃	ISO 11359-2
Vicat Softening Temp	235	℃	ISO 306
Vicat Softening Temp	240	℃	ISO 306
Hot deformation temperature
1.8 MPa, unannealed, 64 mm span	235	℃	ISO 75/Af

PHYSICAL	Nominal value	Unit	Test method
Density	1.65	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	0.25	%	ISO 62
23℃，50% RH	0.05	%	ISO 62
Melt Volume Rate
265℃，1.2 kg	7	cm³/10min	ISO 1133

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	120-130	°C
Drying time	4-6	hrs
Maximum water content	0.02	%
Melt temperature	270-290	°C
Spray nozzle temperature	260-280	°C
Front temperature	270-290	°C
Mid section temperature	260-280	°C
Post stage temperature	250-270	°C
Hopper temperature	40-60	°C
Mold temperature	90-120	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.