| About |
|---|
| 15% glass reinforced Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant. FDA compliant UL-Listing V-0 black at 0.75mm thickness per UL 94 flame testing. UL = Underwriters Laboratories (USA)&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 100 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 252 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 298 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 202 | ℃ | ISO 306 |
| Melting temperature | 335 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | 33 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 2.05 GHz | 3.94 | Internal Method | |
| Dissipation factor | |||
| 2.05 GHz | 5.0E-3 | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 14000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 175 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 2.3 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 14000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 210 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 43 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 6.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 315 to 335 | °C | |
| Barrel middle temperature | 320 to 340 | °C | |
| Barrel front temperature | 325 to 355 | °C | |
| Nozzle temperature | 335 to 350 | °C | |
| Processing (melt) temperature | 335 to 355 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 50.0 to 150 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |