VENYL SG407 - 7731

About
VENYL SG407 – 7731 is a 40 % glass fibre reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SG407 – 7731 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SG407 – 7731 is available in both grey and natural (VENYL SG407) but other colours can be provided on request.&&

About

VENYL SG407 – 7731 is a 40 % glass fibre reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SG407 – 7731 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SG407 – 7731 is available in both grey and natural (VENYL SG407) but other colours can be provided on request.&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	Renewable resources,HB
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.43	g/cm³	ISO 1183
Shrinkage rate	0.30 to 0.70	%
Water absorption rate
Equilibrium, 23 ℃, 50% RH	1.8	%

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	16	kJ/m²	ISO 179
Charpy Unnotch Impact strength	50	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	205	℃	ISO 75-2/A
0.45 MPa, unannealed	215	℃	ISO 75-2/B
Melting temperature
DSC	220	℃	ISO 3146

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+13	ohms	DIN 53482
Volume resistivity	1.0E+14	ohms·cm	DIN 53482
Compared to the leakage tracing index
Solution A	500	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
1.60 mm	HB		UL 94
Glowing wire flammability index
2.0 mm	650	℃	IEC 60695-2-12

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	10500	MPa	ISO 527-2
tensile strength
fracture	195	MPa	ISO 527-2
Tensile strain
fracture	3.0	%	ISO 527-2
Bending modulus	9500	MPa	ISO 178
bending strength	300	MPa	ISO 178
Rockwell hardness
Level L	106		ASTM D785

Process Conditions
injection	Nominal value	Unit	Test method
Barrel rear temperature	245 to 265	°C
Barrel middle temperature	250 to 270	°C
Barrel front temperature	255 to 275	°C
Nozzle temperature	255 to 275	°C
Mold temperature	90 to 120	°C
Injection pressure	85.0 to 110	MPa
Injection speed	Fast
Hold pressure	50.0 to 70.0	MPa
Screw length to diameter ratio	15.0:1.0 to 20.0:1.0

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.