| About |
|---|
| Veradel® PESU was formerly marketed as Gafone™ PESU Veradel® polyethersulfone (PESU) is tranparent and offers high heat deflection temperatures, excellent toughness and dimensional stability, and resistance to steam, boiling water, and mineral acids. Other desirable properties include thermal stability, creep resistance, and inherent flame resistance. Veradel® 3300 is FDA compliant and therefore approved for direct food contact. Veradel® 3200 is a low melt flow grade that can be processed by extrusion or injection molding. Veradel® 3300 is a medium melt flow grade suggested for general purpose injection molding. Veradel® 3400 is a high melt flow grade designed for easy molding of parts with thin walls or long flow lengths.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good Dimensional Stability,Hydrolysis stability,Flame Characteristics,Acidproof,High Heat Resistance,Good bond,Good Tensile Strength,Moderate liquidity,Solvent resistance,Heat Stabilized,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 380℃，2.16kg | 30 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 30days | 1.9 | % | ASTM D570 |
| 24hr | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2690 | MPa | ASTM D638 |
| tensile strength | 88.9 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 6.5 | % | ASTM D638 |
| Bending modulus | 2620 | MPa | ASTM D790 |
| bending strength | 125 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 53 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 200 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 5.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.7E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 15 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.51 | ASTM D150 | |
| 1 kHz | 3.50 | ASTM D150 | |
| 1 MHz | 3.54 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 1.7E-3 | ASTM D150 | |
| 1 kHz | 2.2E-3 | ASTM D150 | |
| 1 MHz | 5.6E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 177 | °C | |
| Drying time | 2.5 | hr | |
| Processing (melt) temperature | 343 to 385 | °C | |
| Mold temperature | 149 to 163 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |