| Veroplas T180 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Europe or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good liquidity,HB |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 91 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 86.1 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 88.0 | % | ASTM D1003 |
| Haze | 4.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 112 | ASTM D785 | |
| tensile strength | |||
| yield | 46.9 | MPa | ASTM D638 |
| Bending modulus | 2340 | MPa | ASTM D790 |
| bending strength | 73.8 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |