| Versaflex™ 9570-9 has exceptional flow properties and surface aesthetics for a variety of applications. Excellent Flow for Long, Thin Flow Paths Exceptional Colorability Overmold Adhesion to Polypropylene Superior Surface Aesthetics&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good liquidity,Good coloring,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 10 seconds | 69 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 23 ℃ | 5.52 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 2.14 | MPa | ASTM D412 |
| 300% Strain, 73°F | 3.45 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 600 | % | ASTM D412 |
| Compression deformation | |||
| 23℃，22 hr | 26 | % | ASTM D395B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.988 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 7.7 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 57 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.90 to 1.6 | % | ASTM D955 |
| Apparent viscosity of melt | ASTM D3835 | ||
| 200℃，1340 sec^-1 | 33.0 | Pa·s | ASTM D3835 |
| 200℃，11200 sec^-1 | 7.40 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 149 to 188 | °C | |
| Barrel middle temperature | 160 to 199 | °C | |
| Barrel front temperature | 171 to 210 | °C | |
| Nozzle temperature | 171 to 210 | °C | |
| Mold temperature | 16 to 27 | °C | |
| Back pressure | 0.00 to 0.689 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 2 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |