| About |
|---|
| Versaflex PKG 4190 Translucent is a translucent semi-hard plastomer made of thermoplastic elastomer and polyethylene, developed for capliner applications. Versaflex PKG 4190 Translucent will give adhesion when melt pressed on lackered metal, provided the lacker is a modified grade for polyethylene adhesion.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Good sensory characteristics. |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，5 kg | 35.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃, 3 seconds | 26 | DIN 53505 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 2 mm | 10.0 | MPa | DIN 53504 |
| Tensile strain | |||
| Fracture, 2 mm | 600 | % | DIN 53504 |
| Compression deformation | |||
| 23℃，72 hr | 25 | % | ISO 815 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 210 | °C | |
| Melt temperature | 160 to 190 | °C | |
| Nozzle temperature | 180 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 7.9 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |