| VERSIFY™ 2200 Plastomer is a resin with a low melt flow rate making it suitable for blown film, blow molding, extrusion and thermoforming. It is an excellent sealant and is particularly suitable for use in BOPE structures. It has excellent compatibility with PP and is an useful agent to bring softness and temperature performance. Main Characteristics Pellet Low Melt Flow Rate Good sealant Compatible with PP Soft polypropylene Applications Blown Film Sealant Soft films BOPE Extrusion Applications Complies with: EU, No 10/2011 U.S. FDA FCN 909 U.S. FDA 21 CFR 175.105(c)(5) Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | POP |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.876 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Summary of crystallinity | 21 | % | Internal Method |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 51 µ m | 86.5 | MPa | ASTM D882 |
| 2% secant, TD: 51 µ m | 94.4 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| Fracture, molded | 20.5 | MPa | ASTM D638 |
| MD, yield, 51 µ m | 10.7 | MPa | ASTM D882 |
| TD, yield, 51 µ m | 10.1 | MPa | ASTM D882 |
| MD, fracture, 51 µ m | 29.5 | MPa | ASTM D882 |
| TD, fracture, 51 µ m | 26.3 | MPa | ASTM D882 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：51 µm | 590 | g | ASTM D1922 |
| TD：51 µm | 1300 | g | ASTM D1922 |
| Initial sealing temperature | |||
| 51 µm | 60.0 | ℃ | Internal Method |
| Final sealing strength temperature | |||
| 50.8 µm | 80 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -24.0 | ℃ | Internal Method |
| Vicat Softening Temp | 63.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 82.2 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D523 | ||
| 20 °, 1000 µ m, molded | 110 | ASTM D523 | |
| 60 °, 1000 µ m, molded | 128 | ASTM D523 | |
| Haze | |||
| 39400 µ m, injection molded film | 4.8 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, molded | 94 | ASTM D2240 | |
| Shaw’s D, molded | 42 | ASTM D2240 | |
| Tensile strain | |||
| Fracture, molded | 690 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 99.9 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Method B |
| 4. Temperatures at which 1 lb/in. (4.4 N/25.4 mm) heat seal strength is achieved. |
| 5. Hardness after 10 seconds. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |