| VERSIFY™ 2300 Elastomer generates the optimum performance balance for blown stretch hoods – the wrapping that ensures the integrity of goods pallets being stored and transported. It provides excellent elasticity and good holding force at equal or better cost than competitor solutions. The film improves pallet stability, delivers better tear resistance and makes recycling and disposal much simpler. The grade is also ideally suited to a range of calendering and extruded applications and as a blend component for thermoplastic elastomers. Complies with: U.S. FDA FCN 909 U.S. FDA 21 CFR 175.105(c)(5) EU, No 10/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.867 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Summary of crystallinity | 13 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -27.0 | ℃ | Internal Method |
| Vicat Softening Temp | 43.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 66.0 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D523 | ||
| 20 °, 1000 µ m, molded | 70 | ASTM D523 | |
| 60 °, 1000 µ m, molded | 109 | ASTM D523 | |
| Haze | |||
| 2000 µ m, injection molding | 6.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, molded | 88 | ASTM D2240 | |
| Shaw’s D, molded | 32 | ASTM D2240 | |
| tensile strength | |||
| Fracture, molded | 18.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 730 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 42.2 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Hardness after 10 seconds. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |