| VERSIFY™ 3401 Elastomer is a resin with a medium melt flow rate suitable for a wide variety of applications and fabrication processes, including cast film, extrusion and injection molding. It is an excellent resin for stretch films and soft films, and is an excellent choice for PP modification, giving consistent performance in hot and cold conditions. Main Characteristics White pellet Free flowing Medium flow Excellent elasticity Excellent compatibility with PP Applications Stretch film Overmolding Soft film PP modification Complies with: EU, No 10/2011 U.S. FDA U.S. FDA FCN 909 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.863 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| Summary of crystallinity | 14 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -29.8 | ℃ | Internal Method |
| Vicat Softening Temp | < 20.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 55.0 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D523 | ||
| 20 °, 1000 µ m, molded | 63 | ||
| 60 °, 1000 µ m, molded | 112 | ||
| Haze | |||
| 2000 µ m, injection molding | 3.2 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, molded | 72 | ||
| Shaw’s D, molded | 22 | ||
| tensile strength | |||
| Fracture, molded | 6.80 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 600 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 22.7 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Hardness after 10 seconds. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |