| Versollan™ RU 2205-1 is a high performance, injection moldable TPU alloy developed to offer a rubbery feel and appearance, reduced cycle times, and performance properties associated with TPUs. Bonds to PC, ABS, PC/ABS, and Copolyester Excellent Abrasion Resistance Fast Set Up Rates During Processing Matte Finish Rubbery, Soft Touch Feel Very Good Oil Resistance&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Good wear resistance,Grease resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.0 | % | ASTM D995 |
| TD | 1.5 | % | ASTM D995 |
| water content | |||
| viscosity | 14.1 | Pa·s | ASTM D3835 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.0 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 67 | g/10min | ASTM D1238 |
| Maximum value | 0.020-0.030 | ||
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -67.0 | ℃ | ASTM D746 |
| Linear coefficient of thermal expansion |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Screw speed | 75-125 | rpm | |
| Regional availability | 非洲和中东，亚太地区，欧洲，北美，南美 | ||
| rohs compliance | 通过无铅认证 | ||
| Suggest maximum grinding degree | 20 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shaw’s A10s | 65 | ASTM D2240 | |
| tensile strength | 13.8 | MPa | ASTM D412 |
| tensile strength | 2.62 | MPa | ASTM D412 |
| tensile strength | 4.21 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 710 | % | ASTM D412 |
| tear strength | 47.3 | kN/m | ASTM D624 |
| Compression deformation | 34 | % | ASTM D395B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 51.7 -54.4 | °C | |
| Drying time | 3.00-4.00 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 168-188 | °C | |
| Central temperature of the barrel | 179-199 | °C | |
| Barrel front temperature | 191-210 | °C | |
| Die temperature | 191-216 | °C | |
| Mold temperature | 21.1-32.2 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 2 hr |
| 4. Thickness = 1.91mm Conditioned for 40hrs at 23C at 50% RH |
| 5. 1.5mm for US and China; 3.0mm for Canada. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |