| About |
|---|
| Versollan™ RU 2205-9 is a high performance, injection moldable TPU alloy developed to offer a rubbery feel and appearance, reduced cycle times, and performance properties associated with TPUs. Bonds to PC, ABS, PC/ABS, and Copolyester Excellent Abrasion Resistance Fast Set Up Rates During Processing Matte Finish Rubbery, Soft Touch Feel Very Good Oil Resistance&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Good wear resistance,Grease resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 10 seconds | 65 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 23 ℃ | 13.8 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 2.62 | MPa | ASTM D412 |
| 300% Strain, 73°F | 4.21 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 710 | % | ASTM D412 |
| tear strength | 47.3 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 34 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -67.0 | ℃ | ASTM D746 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 7.0 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 67 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.0 to 1.5 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃，11200 sec^-1 | 14.1 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 52 to 54 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.030 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 168 to 188 | °C | |
| Barrel middle temperature | 179 to 199 | °C | |
| Barrel front temperature | 191 to 210 | °C | |
| Nozzle temperature | 191 to 216 | °C | |
| Processing (melt) temperature | 188 to 210 | °C | |
| Mold temperature | 21 to 32 | °C | |
| Back pressure | 0.00 to 0.862 | MPa | |
| Screw speed | 75 to 125 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 2 hr |
| 4. Thickness = 1.91mm Conditioned for 40hrs at 23C at 50% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |