| About |
|---|
| Unfilled polyamid 12 compounds Characterization: high viscosity, heat and light stabilized Application Examples: Transparent sports shoe soles, ski cover films The properties of PA 12 compounds can be modified to suit the requirements of many applications by incorporating various additives such as stabilizers, plasticizers, reinforcements, and fillers. The VESTAMID® L compounds of Evonik comprise a range of various products that are customized to the requirements of processors and users. Many of the PA 12 compounds are suitable especially for the injection molding of recision parts; others have been developed specifically for the extrusion process.&& |
| Product Description | |
|---|---|
| Supplier | Evonik |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,High impact resistance,High Viscosity,Low or no water absorption,noise reduction,Food contact compliance,Fatigue resistance,Good wear resistance,Grease resistance,Solvent resistance,Heat Stabilized,High ESCR,Fuel resistance,HB |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.4 | % | ISO 294-4 |
| MD | 1.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.80 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1100 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 46.0 | MPa | ISO 527-2 |
| yield | 37.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 |
| yield | 5.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30 ℃, completely fractured | 13 | kJ/m² | ISO 179/1eA |
| 23 ℃, completely fractured | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 45.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 170 | ℃ | ISO 306/A |
| — | 130 | ℃ | ISO 306/B |
| Melting temperature | 176 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 1.3E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 24 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 23℃，100 Hz | 3.80 | IEC 60250 | |
| 23℃，1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 23℃，100 Hz | 0.053 | IEC 60250 | |
| 23℃，1 MHz | 0.028 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA12, EHL, 22-010 | ISO 1874 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |