| About |
|---|
| VESTOLIT G 215 is a low molecular weight particle size homopolymer blending resin intended for use in plastisol formulations. It improves air release performance resulting in reduced scrap rates. It decreases high shear viscosity providing an improved ‘ease of coating’ performance resulting in a more uniform plastisol coating and improving line up time. It reduces viscosity aging characteristics, providing increased plastisol usage (pot life). It reduces surface gloss of films or coated products resulting in less surface blocking and improved handling. VESTOLIT G 215 is recommended for solid and foamed plastisol applications such as coated fabric, cast films and coatings, foam mats and pads.&& |
| Product Description | |
|---|---|
| Generic | PVC homopolymer |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| optical performance | Nominal value | Unit | Test method |
| Haze | |||
| Fused 5 mins，177℃ | 20 | % | Internal Method |
| gloss | |||
| 60 Degree Fused 5 mins @ 350F | 20 | % | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Residual Vinyl Chloride Monomer | < 5 | ppm | Internal Method |
| volatility | 0.060 | % | Internal Method |
| polymerization process | 悬挂 | ||
| Gel temperature | |||
| PP | 78 | ℃ | Internal Method |
| Vinyl diffusion meter | 75.0 | µm | Internal Method |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ASTM D792 |
| K-Value | 64.0 | Internal Method | |
| Apparent density of loose states | 0.430 | g/cm³ | Internal Method |
| Intrinsic viscosity | 0.85 | ASTM D1243-60-A | |
| Particle size | Internal Method | ||
| < 52 Micron | 98.0 | % | Internal Method |
| < 74 Micron | 99.8 | % | Internal Method |
| Average particle size | 25.0 | µm | Internal Method |
| Relative viscosity | 2.12 | Internal Method | |
| Brookfield viscosity | Internal Method | ||
| Initial viscosity @ 2 rpm | 3.40 | Pa·s | Internal Method |
| Initial viscosity @ 2 rpm | 3.50 | Pa·s | Internal Method |
| One day viscosity @ 2 rpm | 4.00 | Pa·s | Internal Method |
| One day viscosity @ 20 rpm | 4.23 | Pa·s | Internal Method |
| Cut off the outflow | |||
| 95 psi | 276.00 | g/10 min | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Correlation, 0.5g/100ml |
| 3. VESTOLIT STP 1169 |
| 4. VESTOLIT DFT 1466 |
| 5. Correlation, Cyclohexanone 1% |
| 6. VESTOLIT ALTC 65 (with provided formulation) |
| 7. VESTOLIT ALTC 66 (with provided formulation) |
| 8. VESTOLIT ALTC 22 (with provided formulation) |
| 9. VESTOLIT ALTC 23 (with provided formulation) |
| 10. VESTOLIT ALTC 29 (with provided formulation) |
| 11. VESTOLIT STP 1005 |
| 12. VESTOLIT STP 1203 (with provided formulation) |
| 13. VESTOLIT STP 1242 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |