| About |
|---|
| VIBRATHANE® B600, B601 and B602 are polyether-based (PTMG) liquid polymers which will produce elastomers in the hardness range 80 to 95 Shore A (30 to 50 Shore D) when cured with 4,4′-methylene-bis-(orthochloroaniline), commonly called MOCA. Features of these elastomers include: Good toughness and abrasion resistance. Excellent low temperature flexibility. Very good dynamic properties High resilience. Good resistance to heat, humidity and many other environments. Low viscosity and easy processing characteristics.&& |
| Product Description | |
|---|---|
| Supplier | Chemtura |
| Generic | PUR-脂肪族+TDI |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Low Viscosity,Elastic,Low temperature toughness,Good wear resistance,Heat Resistance, Good |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 90 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| 100% strain | 7.58 | MPa | ASTM D412 |
| 300% strain | 15.2 | MPa | ASTM D412 |
| tensile strength | 37.9 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 430 | % | ASTM D412 |
| tear strength | |||
| — | 105 | kN/m | ASTM D624 |
| cracking | 16 | kN/m | ASTM D470 |
| Compression deformation | |||
| 70℃，22 hr | 30 | % | ASTM D395B |
| Basho’s elasticity | 42 | % | ASTM D2632 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -63.0 | ℃ | ASTM D746 |
| Thermosetting components | |||
| resin | 按重量计算的混合比: 100 | ||
| Hardening method | 按重量计算的混合比: 12 | ||
| storage stability | 10 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |