| About |
|---|
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Negative |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile Strength | |||
| 23 ° C, yield yld | 95 | MPa | ISO 527 |
| -196 ° C, fracture brk | 200 | MPa | ISO 527 |
| Elongation at Break | |||
| 23°C | 70 | % | ISO 527 |
| -196°C | 8 | % | ISO 527 |
| Flexural Strength | |||
| 23°C | 150 | MPa | ISO 178 |
| -196°C | 435 | MPa | ISO 178 |
| Flexural Modulus | |||
| 23°C | 3500 | MPa | ISO 178 |
| -196°C | 5400 | MPa | ISO 178 |
| Compressive Strength | |||
| 23°C | 120 | MPa | ISO 604 |
| -196°C | 305 | MPa | ISO 604 |
| Shore hardness | |||
| 23°C | 84 | ISO 868 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting point | 343 | ℃ | ISO 11357 |
| Glass Transition Temperature | |||
| Onset | 143 | ℃ | ISO 11357 |
| Coeff. of linear thermal expansion | |||
| 45 | ppm /K | ISO 11359 | |
| 65 | ppm /K | ISO 11359 | |
| Thermal conductivity | |||
| Average, 23°C | 0.29 | W/m/K | ISO 22007-4 |
| Along flow, 23°C | 0.32 | W/m/K | ISO 22007-4 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt viscosity | |||
| 400°C | 550 | Pa.s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120-150 | ℃ | |
| Nozzle temperature | 395 | °C | |
| Hopper Temperature | ≤100 | °C | |
| Mold Temperature | 170 – 200 | °C | |
| Drying Time | 3-5 | hr | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |