| About |
|---|
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Solvent resistance,Good wear resistance,Good liquidity,Hypocrystalline,Good Rigidity,Food contact compliance |
| Availabilitys | Africa & Middle East ,Latin America,North America,Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore D, 23 ℃ | 88 | ISO 868 | |
| Tensile Modulus | |||
| 23℃ | 28000 | MPa | ISO 527-2 |
| Tensile Strength | ISO 527-2 | ||
| Broken BRK, 23 ℃ | 275 | MPa | ISO 527-2 |
| Broken BRK, 125 ℃ | 170 | MPa | ISO 527-2 |
| Broken BRK, 175 ℃ | 110 | MPa | ISO 527-2 |
| Broken BRK, 225 ℃ | 80.0 | MPa | ISO 527-2 |
| Broken BRK, 275 ℃ | 70.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, 23 ℃ | 1.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23℃ | 23500 | MPa | ISO 178 |
| Flexural Strength | ISO 178 | ||
| 23℃ | 400 | MPa | ISO 178 |
| 125℃ | 265 | MPa | ISO 178 |
| 175℃ | 185 | MPa | ISO 178 |
| 275℃ | 100 | MPa | ISO 178 |
| Compressive Strength | ISO 604 | ||
| 23℃ | 300 | MPa | ISO 604 |
| 120℃ | 210 | MPa | ISO 604 |
| 200℃ | 95.0 | MPa | ISO 604 |
| 250℃ | 65.0 | MPa | ISO 604 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 45 | kJ/m² | ISO 179/1U |
| Izod Notched Impact strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 180-A |
| Izod Unnotched Impact strength of cantilever beam | |||
| 23℃ | 50 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 368 | ℃ | ISO 75-2/Af |
| Glass Transition Temperature | ISO 11357-2 | ||
| — | 152 | ℃ | ISO 11357-2 |
| — | 160 | ℃ | ISO 11357-2 |
| Melting temperature | 373 | ℃ | ISO 11357-3 |
| Coeff. of linear thermal expansion | |||
| TD | ISO 11359-2 | ||
| < 152℃ | 3.5E-5 | cm/cm/℃ | ISO 11359-2 |
| > 152℃ | 9.0E-5 | cm/cm/℃ | ISO 11359-2 |
| MD | ISO 11359-2 | ||
| > 152℃ | 5.0E-6 | cm/cm/℃ | ISO 11359-2 |
| < 152℃ | 5.0E-6 | cm/cm/℃ | ISO 11359-2 |
| Thermal conductivity | ISO 22007-4 | ||
| 23℃ | 0.95 | W/m/K | ISO 22007-4 |
| 23℃ | 2.1 | W/m/K | ISO 22007-4 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | |||
| 23℃ | 1.0E+5 | ohms·cm | ASTM D4496 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glow Wire Flammability Index GWFI | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Spiral flow length | 8.00 | cm | Internal Method |
| Molding shrinkage | ISO 294-4 | ||
| TD | 0.70 | % | ISO 294-4 |
| MD | 0.10 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation, 23 ℃ | 0.50 | % | ISO 62 |
| Saturation, 100 ℃ | 0.60 | % | ISO 62 |
| Apparent viscosity | |||
| 400℃ | 525 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature Zone 1 | 380 | °C | |
| Middle Temperature Zone 2 | 390 to 395 | °C | |
| Front Temperature Zone 3 | 400 | °C | |
| Nozzle temperature | 405 | °C | |
| Mold Temperature | 190 to 215 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |