| About |
|---|
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Good disinfection,Good liquidity,Low CLTE,Hypocrystalline,Solvent resistance,Food contact compliance,Good Rigidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding shrinkage | |||
| MD | 0.30 | % | ISO 294-4 |
| TD | 0.90 | % | ISO 294-4 |
| Water Absorption | |||
| 23℃，24hr | 0.05 | % | ISO 62 |
| 23℃，50% RH | 0.40 | % | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, annealed | 323 | ℃ | ISO 75-2/Af |
| Melting temperature | 343 | ℃ | ISO 11357-3 |
| Glass Transition Temperature | 143 | ℃ | ISO 11357-2 |
| Vicat Softening Temperature | |||
| Coeff. of linear thermal expansion | |||
| MD | 2.5E-5 | 1/℃ | ISO 11359-2 |
| TD | 4.5E-5 | 1/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1.0E+16 | Ω.cm | IEC 60093 |
| Insulation Strength | |||
| 23 | KV/mm | IEC 60243-1 | |
| Dielectric Constant | |||
| 23℃ | 3.20 | 1 MHz | IEC 60250 |
| Dissipation Factor | |||
| 23℃ | 4.0E-3 | 1 MHz | IEC 60250 |
| Compared Tracking Index | 150 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.50mm | V-0 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 86 | ISO 868 | |
| Tensile Strength | |||
| 23℃ | 150 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, 23 ℃ | 2.4 | % | ISO 527-2 |
| Tensile Modulus | |||
| 23℃ | 9000 | MPa | ISO 527-2 |
| Flexural Strength | |||
| 23℃ | 240 | MPa | ISO 178 |
| Flexural Modulus | |||
| 23℃ | 8500 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 -150 | °C | |
| Drying Time | 3.0-5.0 | Hr | |
| Rear Temperature Zone 1 | 365 | ℃ | |
| Middle Temperature Zone 2 | 370 | ℃ | |
| Front Temperature Zone 3 | 380 | ℃ | |
| Die temperature | 385 | ℃ | |
| Mold Temperature | 180-210 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |