| High performance thermoplastic material, 40% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, FDA food contact compliant, colour black. Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.&& |
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Food contact compliance,Low liquidity,Solvent resistance,Good Rigidity,Good wear resistance,Hypocrystalline |
| Availabilitys | North America,Africa & Middle East ,Asia Pacific,Latin America,Europe |
| Process Methods | Injection Molding,Extrusion |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 45 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 143 | ℃ | ISO 3146 |
| Melting temperature | 343 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：< 143℃ | 5.0E-6 | 1/℃ | |
| MD：> 143℃ | 8.0E-6 | 1/℃ | |
| TD：< 143℃ | 3.5E-5 | 1/℃ | |
| TD：> 143℃ | 9.0E-5 | 1/℃ | |
| Specific heat capacity | 1800 | J/kg/℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+5 | ohms·cm | ASTM D4496 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| toxicity | NES 713 | ||
| CO Content | 0.0500 | ||
| CO2 Content | 0.120 | ||
| Total Gases | 0.170 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 88 | ISO 868 | |
| Tensile modulus | |||
| 23℃ | 35000 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 270 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.4 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 30000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 400 | MPa | ISO 178 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Spiral flow length | 6.50 | cm | Internal Method |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | |
| MD：200℃ | 0.10 | % | |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr，3.20 mm | 0.030 | % | |
| Equilibrium, 23 ℃, 50% RH, 3.20 mm | 0.30 | % | |
| Apparent viscosity of melt | |||
| 400℃ | 850 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 150 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Hopper temperature | < 100 | °C | |
| Barrel rear temperature | 380 | °C | |
| Barrel middle temperature | 390 to 395 | °C | |
| Barrel front temperature | 400 | °C | |
| Nozzle temperature | 405 | °C | |
| Mold temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Crystalline |
| 3. Mold Temperature: 392°F, Melt Temperature: 761°F |
| 4. 1 mm |
| 5. 405°C nozzle, 200°C tool |
| 6. Onset |
| 7. Midpoint |
| 8. 1V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |