| About |
|---|
| High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for compression moulding, standard flow, FDA food contact compliant, colour natural.&& |
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Hypocrystalline,Good liquidity |
| Availabilitys | Asia Pacific,Europe,Africa & Middle East ,North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 4000 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 98.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 30 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 3800 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 160 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.0 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | No Break | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | ISO 11357-2 | ||
| — | 143 | ℃ | ISO 11357-2 |
| — | 150 | ℃ | ISO 11357-2 |
| Melting temperature | 343 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Compression molding temperature | 380 to 400 | ℃ | |
| drying temperature | |||
| Compression molding | 120 to 150 | ℃ | |
| drying time | |||
| Compression molding | 3.0 to 5.0 | hr |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Apparent density | 0.30 | g/cm³ | ISO 1183 |
| Average particle size | |||
| d50 | 50 | µm | ISO 13320-1 |
| Apparent viscosity of melt | |||
| 400℃ | 350 | Pa·s | ISO 11443 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Onset |
| 3. Midpoint |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |