| About |
|---|
| High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, FDA food contact compliant, colour black. Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.&& |
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Hypocrystalline,Low liquidity,Low coefficient of friction,Good wear resistance,Solvent resistance,Good Rigidity |
| Availabilitys | North America,Europe,Africa & Middle East ,Latin America,Asia Pacific |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 25000 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Fracture, 23 ℃ | 250 | MPa | ISO 527-2 |
| Fracture, 125 ℃ | 150 | MPa | ISO 527-2 |
| Fracture, 175 ℃ | 85.0 | MPa | ISO 527-2 |
| Fracture, 275 ℃ | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.9 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 21500 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| 23℃ | 370 | MPa | ISO 178 |
| 125℃ | 250 | MPa | ISO 178 |
| 175℃ | 120 | MPa | ISO 178 |
| 275℃ | 60.0 | MPa | ISO 178 |
| compressive strength | ISO 604 | ||
| 23℃ | 280 | MPa | ISO 604 |
| 120℃ | 180 | MPa | ISO 604 |
| 200℃ | 60.0 | MPa | ISO 604 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 60 | kJ/m² | ISO 179/1U |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 60 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 333 | ℃ | ISO 75-2/Af |
| Glass transition temperature | ISO 11357 | ||
| — | 143 | ℃ | ISO 11357 |
| — | 150 | ℃ | ISO 11357 |
| Melting temperature | 343 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：< 143℃ | 6.0E-6 | 1/℃ | ISO 11359-2 |
| MD：> 143℃ | 6.0E-6 | 1/℃ | ISO 11359-2 |
| TD：< 143℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：> 143℃ | 1.4E-4 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | ISO 22007-4 | ||
| 23℃ | 0.95 | W/m/K | ISO 22007-4 |
| 23℃ | 2.0 | W/m/K | ISO 22007-4 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+5 | ohms·cm | IEC 60093 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Spiral flow length | Internal Method | ||
| — | 8.00 | cm | Internal Method |
| — | 37.5 | cm | Internal Method |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | 0.10 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.30 | % | ISO 62 |
| Saturation, 100 ℃ | 0.45 | % | ISO 62 |
| Apparent viscosity of melt | |||
| 420℃ | 800 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 150 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Hopper temperature | < 100 | °C | |
| Barrel rear temperature | 390 | °C | |
| Barrel middle temperature | 400 to 405 | °C | |
| Barrel front temperature | 410 | °C | |
| Nozzle temperature | 415 | °C | |
| Mold temperature | 180 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Crystalline |
| 3. Mold Temperature: 392°F, Melt Temperature: 779°F |
| 4. 1 mm |
| 5. 3 mm |
| 6. 415°C nozzle, 200°C tool |
| 7. Onset |
| 8. Midpoint |
| 9. Average |
| 10. Along flow |
| 11. 1V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |